NASA Tests Bimetallic 3D-Printed Rocket Engine Prototype Part
The 3D-printed rocket engine igniter can be made faster, cheaper and more reliably than the traditional brazed part.
Graduate students Chris Hill and Ryan Anderson, along with Marshall Space Flight Center advanced manufacturing chief Majid Babai and University of Alabama in Huntsville mechanical and aerospace engineering professor Dr. Judy Schneider examine a cross-section of the bimetallic, 3D-printed prototype rocket engine igniter.
The hybrid 3D printing process used to manufacture the rocket engine igniter prototype creates a strong bond between the copper alloy and Inconel.
Engineers at NASA's Marshall Space Flight tested NASA's first 3D-printed rocket engine prototype part made of two different metal alloys. NASA has been making and evaluating 3D-printed parts made of one metal, but 3D printing with more than one metal is more difficult.
According to Marshall’s director of the engineering directorate Preston Jones, the process could reduce future rocket engine costs by up to a third and manufacturing time by 50 percent.
Featured Content
Engineers low-pressure hot-fire tested the prototype more than 30 times to demonstrate its functionality. The prototype, built by a commercial vendor, was then cut up by University of Alabama in Huntsville researchers who examined images of the bimetallic interface through a microscope. The results showed the two metals had inter-diffused, helping create a strong bond.
Rocket engine igniters are used to initiate an engine’s start sequence. They are traditionally built using a process called brazing, which joins two types of metals by melting a filler metal into a joint to create a bimetallic component. The brazing process requires a significant amount of manual labor, leading to high costs and long manufacturing time.
In addition to decreasing cost and manufacturing time, building bimetallic parts in a single machine decreases risk by increasing reliability. Because the bond between the two materials is generated internally, hard transitions that could cause the component to crack under the forces and temperature gradient of space travel are eliminated.
A copper alloy and Inconel were joined together using a hybrid process called automated blown powder laser deposition. Traditionally made of four parts that are brazed and welded together, the prototype was created during a single build process using a DMG MORI hybrid machine. While the igniter is only 10 inches tall and 7 inches at its widest diameter, this new technology enables larger parts and machining of the interior of parts during manufacturing.
Related Content
-
Sinter-Based Additive Manufacturing Finds a Place Alongside MIM, Press and Sinter at APG
Powder metallurgy company Alpha Precision Group (APG) is applying a particular class of metal 3D printing technology for both rapid iteration in development and flexibility in production.
-
4 Ways Augmented Reality and 3D Printing Intersect
Augmented reality (AR) is bringing benefits to additive manufacturing, and vice-versa.
-
Faster Iteration, Flexible Production: How This Inflation System OEM Wins With 3D Printing
Haltec Corp., a manufacturer of tire valves and inflation systems, finds utility in 3D printing for rapid prototyping and production of components for its modular and customizable products.